曾建,马年方,李昱,李锦荣,陈瑞荣,梁磊.蔗渣纤维模板法制备纤维状氧化铁[J].广西科学,2016,23(1):56-61. [点击复制]
- ZENG Jian,MA Nianfang,LI Yu,LI Jinrong,CHEN Ruirong,LIANG Lei.Synthesis of Fibrous Iron Oxide with Bagasse Fiber as the Template[J].Guangxi Sciences,2016,23(1):56-61. [点击复制]
|
|
| 本文已被：浏览 407次 下载 362次 |
码上扫一扫！ |
| 蔗渣纤维模板法制备纤维状氧化铁 |
|
曾建, 马年方, 李昱, 李锦荣, 陈瑞荣, 梁磊
|
|
|
| (广州甘蔗糖业研究所, 广东省甘蔗改良与生物炼制重点实验室, 广州市植物纤维综合利用重点实验室, 广东省生物质高值化利用工程实验室, 广东省植物纤维综合利用工程技术研究开发中心, 广东广州 510316) |
|
| 摘要: |
| [目的]探寻蔗渣纤维作为模板材料制备纤维状无机材料的可行性,寻找蔗渣高值化利用的新方法。[方法]利用碱/双氧水法处理蔗渣纤维,再以不同阶段的蔗渣纤维为基体,模板法制备纤维状的氧化铁。[结果]蔗渣纤维处理前的直径为100~150μm,处理后蔗渣纤维素纤维的直径为10~30μm;碱/双氧水法处理过程中,蔗渣纤维灰分降低;模板法制备的氧化铁纤维的直径为5~30μm。[结论]蔗渣纤维向蔗渣纤维素纤维转变过程中,纤维直径和纤维结构发生明显变化;蔗渣纤维作为模板材料制备纤维状无机材料可行,且方法简易。 |
| 关键词: 蔗渣纤维 纤维状氧化铁 无机材料 |
| DOI：10.13656/j.cnki.gxkx.20160315.016 |
| 投稿时间：2015-11-20修订日期：2016-01-10 |
| 基金项目:广东省科技计划项目(2015A010105018,2013B06060001),国家自然科学基金项目(51303030),广东省科学院专项资金项目(2016GDASPT-0108),科技部院所技术开发研究专项资金项目(2013EG111222)和转制院所创新能力专项资金项目(2014EG111227)资助。 |
|
| Synthesis of Fibrous Iron Oxide with Bagasse Fiber as the Template |
|
ZENG Jian, MA Nianfang, LI Yu, LI Jinrong, CHEN Ruirong, LIANG Lei
|
| (Guangdong Key Lab of Sugarcane Improvement & Biorefinery, Guangzhou Key Laboratory for Comprehensive Utilization of Plant Fiber, Guangdong Provincial Engineering Laboratory of Biomass High Value Utilization, Guangdong Provincial Engineering Technology Research and Development Center of Biomass Comprehensive Utilization, Guangzhou Sugarcane Industry Research Institute, Guangzhou, Guangdong, 510316, China) |
| Abstract: |
| [Objective] The preparation of fibrous inorganic materials with bagasse fiber as the template was explored to look for new method of high value utilization of bagasse.[Methods] Bagasse fibres were treated by alkali/peroxide, and the changes in the structure and ash content of bagasse fibers were studied in the extraction process of cellulose from bagasse.The iron oxide fibers were prepared by high temperature calcination with the different bagasse fibers as the template.[Results] The results revealed that the mean diameter of bagasse fibers, bagasse cellulose fibers and iron oxide fibers was 100~150μm, 10~30μm and 5~30μm, respectively.The ash content of bagasse fibers decreased in the process of alkali/peroxide treatment.[Conclusion] The fiber diameter and structure of bagasse fibers and bagasse cellulose fibers were significantly different in the transformation from bagasse fibers to bagasse cellulose fibers.The preparation of fibrous inorganic materials with bagasse fibers as the template is completely feasible and simple. |
| Key words: bagasse fibers iron oxide fibers inorganic materials |